NACORR 1352 is a liquid corrosion inhibitor based on the calcium salt of an aromatic sulfonic acid. It is compatible with waterborne and solventborne systems and offers an excellent balance of compatibility and performance.
| Metal Type | Calcium |
| % Active | 50 |
| Solvent | 2-Butoxyethanol |
| Application Advantage | Corrosion resistance, Gloss, Pigment dispersion |
| Formulation Advantage | Synergistic with ACP |
| Market Application | Air dry, General industrial, Maintenance, Primers, Thermoset, Waterborne |
| Product Group | Corrosion inhibitor |
Related Products
-
NACORR 1552
Metal Type Zinc% Active 50Solvent 2-ButoxyethanolCorrosion inhibitorLiquid corrosion inhibitor offering excellent adhesion for solvent based primers. Catalytic in amino systems. Best synergy with Zinc ACPs. -
NACORR 1652
Metal Type Magnesium% Active 50Solvent 2-ButoxyethanolCorrosion inhibitorLiquid corrosion inhibitor providing excellent DTM adhesion. Excellent performance in waterborne primers. -
NACORR 1389
Metal Type Calcium% Active 45Solvent 2-ButoxyethanolCorrosion inhibitorLiquid corrosion inhibitor that is effective in both waterborne and solventborne coatings. Improves corrosion resistance and water resistance. -
NACORR 1351
Metal Type Calcium% Active 50Solvent Mineral SpiritsCorrosion inhibitorLiquid corrosion inhibitor. Promotes pigment dispersion when a small amount is used in the grind, which reduces grind time, increases pigment loading, and improves color strength. -
NACORR 1151
Metal Type Barium% Active 50Solvent Mineral SpiritsCorrosion inhibitorLiquid corrosion inhibitor with excellent performance in in solventborne and waterborne systems. Recommended for low pH systems.
Recently Viewed Products
-
K-CORR 100
Mineral Oil Content 0%Acid Value 107 mg KOH/gViscosity @ 40°C 470 cStRust inhibitorAshless rust inhibitor and intermediate. -
NACORR 1552
Metal Type Zinc% Active 50Solvent 2-ButoxyethanolCorrosion inhibitorLiquid corrosion inhibitor offering excellent adhesion for solvent based primers. Catalytic in amino systems. Best synergy with Zinc ACPs. -
K-FLEX XM-337
Viscosity @ 25°C 55,000 cPsHydroxyl Number 220Equivalent Weight, g/eq. (as supplied) 260Polyester diolImproves flexibility, impact resistance and chemical resistance. Excellent UV durability. Recommended for urethane and blocked isocyanate systems.